The structure, morphology and magnetic properties of Sr-ferrite powder prepared by the molten-salt method

Keyphrases

• Structure-property Relationships 100%
• Magnetic Properties 100%
• Morphological Properties 100%
• Morphological Structure 100%
• Molten Salt Method 100%
• Sr-ferrite 100%
• Ferrite Powders 100%
• Coercivity 40%
• Reaction Parameters 20%
• Annealing 20%
• Particle Size 20%
• High Performance 20%
• Saturation Magnetization 20%
• Enlargement 20%
• Reaction Process 20%
• Annealing Temperature 20%
• Sodium Sulfate 20%
• Magnetocrystalline Anisotropy 20%
• Particle Size Effect 20%
• Hexagonal Ferrites 20%
• Maximum Magnetic Energy Product 20%
• Remanence Ratio 20%
• Annealing Time 20%
• Pre-sintering Temperature 20%
• Magnetic Performance 20%
• Magnetoplumbite Structure 20%
• Fluxing Agent 20%
• BaFe12O19 20%
• Traditional Ceramics 20%
• Demagnetization Factor 20%
• Ceramic Technique 20%
• Superfine Powder 20%
• Sub-micrometer 20%

Material Science

• Magnetic Property 100%
• Molten Salt Method 100%
• Annealing 33%
• Sintering Temperature 33%
• Anisotropy 33%
• Pre-Sintering 33%
• Fluxing Agent 33%