Mechanical property enhancements and amorphous thermal transports of ordered weberite-type RE₃Nb/TaO₇ high-entropy oxides

Keyphrases

• A-site 50%
• B-site 50%
• Coating Materials 100%
• Coefficient of Thermal Expansion 50%
• Energy Dispersive Spectrometry 50%
• Fracture Toughness KIC 50%
• Grain Refinement 50%
• High Stiffness 50%
• High Thermal Expansion 50%
• High-entropy Oxides 100%
• Long-range Ordering 50%
• Low Thermal Conductivity 50%
• Mechanical Properties Enhancement 100%
• Nb Oxide 50%
• Nb-Ta 50%
• Ordered Arrangement 50%
• Phase Stability 50%
• Protective Coatings 100%
• Rare Earth 50%
• Rare Earth Niobates 50%
• Rare-earth Cations 50%
• Scanning Electron Microscopy 50%
• Solid Solution Strengthening 50%
• Stiffness 50%
• Ta Oxide 50%
• Tantalate 50%
• Thermal Conductivity 50%
• Thermal Transport 100%
• Toughness 50%
• Transmission Electron Microscopy 50%
• Weberite 100%
• X Ray Diffraction 50%

Material Science

• Fracture Toughness 50%
• Grain Refinement 50%
• High-entropy Oxides 100%
• Niobate 50%
• Oxide Compound 50%
• Protective Coating 100%
• Scanning Electron Microscopy 50%
• Solid Solution 50%
• Tantalate 50%
• Thermal Conductivity 100%
• Thermal Expansion 50%
• Transmission Electron Microscopy 50%
• X-Ray Diffraction 50%

Engineering

• Coating Material 100%
• Energy dispersive spectrometry 50%
• Expansion Coefficient 50%
• Fracture Strength 50%
• Low Thermal Conductivity 50%
• Phase Stability 50%
• Potential Application 50%
• Ray Diffraction 50%
• Solid Solution 50%
• Structure Type 50%
• Thermal Conductivity 50%